Surface Treated Sulphur

Surface Treated Sulphur
Surface Treated Sulphur
Product Code : 76
Product Description

With the employment of advanced technology and innovative tools, we offer an excellent quality of Surface Treated Sulphur. The provided sulphur is carefully formulated by mixing standard quality copper sulfate and sodium carbonate in line with the set industry norms of quality. Owing to its accurate composition and long shelf life, this sulphur is widely acclaimed amongst clients. Available in granule and powder form, this Surface Treated Sulphur is broadly used as a fertilizer in agriculture industry and is used in the manufacturing of rubber.

Features:

  • Avoids blooming during storage of green compound.

  • No formation of aggregates appears in the rubber avoiding local over cure.

  • Improved dispersion provides higher physical properties, both before and after aging.

  • In dynamic applications it provides higher service life. E.g. in rice dehusking rollers. Due to local burning and presence of phenolic resin in the product, failure of the product can be earlier and erratic. Proper dispersion of sulphur avoids such failure.

  • In colored applications, uniform dispersion of sulphur is very important, which is provided by CCS. Due to this brown spots are not observed on the surface.

Chemical Composition:
  • Material: Treated / Modified Sulphur

  • Appearance: Yellow Powder

  • Ash, %: 1.0 Max.

  • Mesh Size: 200 Min.

  • Moisture, %: 1.0 Max.

Function:

Sulphur Dispersion has always been problem for rubber industry. This is particularly true for Nitrile Rubber, to some extent Polychloroprene and EPDM Rubber.

CCS has been electrically / chemically surface treated to avoid agglomeration. This electric charge allows the particles to disperse well in rubber matrix. It very effectively replaces Magnesium Carbonate Coated Sulphur.

Typical Applications:

  • Rice Dehusking Rollers

  • Football Cover

  • Textile Cots and Aprons

  • LPG Tubing

  • Textile blankets and Rolls

  • Oil Seals and O Rings based on NBR.

Mixing Cycle:

CCS treated sulphur should be mixed as usually followed for various rubbers. For Nitrile Rubber, it should be added immediately after rubber is warmed up and forms the band on the mill. For soft compounds, it can be added at the last stage of mixing. Tight nip refining will help further improvement in dispersion of CCS.

Please find below the classic example of ageing properties and compounding comparison:

Formula:
Nitrile Rubber (Medium): 100, ZnO: 5, Strearic Acid: 1, HAF: 30, Clay: 10, DOP: 10, CBS: 1.2, TMT: 0.2, Sulphur: 1.5

Rheometric Test Report at 150oC

MC

CCS

  • Scroch Time, Ts2, Mins.
  • Cure Time, Tc90, Mins.
  • T Min., In LBS.
  • T Max., In LBS.

03.94
20.67
11.61
68.84

04.17
21.39
11.57
67.96

Curing Temp oC / Time Min.

150/20

150/20

  • Hardness (Shore A)
  • Tensile Strength (kg/cm2)
  • Elongation at break (%)
  • Modulus: 300% (kg/cm2)

62
162
550
56

62
171
580
48

Physical Testing After Ageing at 100oC for 48 hrs.


  • Hardness (Shore A)
  • Tensile Strength (kg/cm2)
  • Elongation at break (%)
  • Modulus: 300% (kg/cm2)

68
144
410
100

67
162
490
88

Compression Set at 70oC for 48 hrs, 25% Deflection (%)

34.20

30.10

*Observation Remarks: Better physicals are observed with CCS over MC Sulphur.


Formula:
Nitrile Rubber (Medium): 100, ZnO: 5, Strearic Acid: 1, HAF (N-330): 35, DOP: 10, CBS: 1.2, TMTD: 0.2, Sulphur: 1.5

Properties

Normal MC

SCCARE CCS

6-ppd
TDQ
Physical Testing Before Ageing
Cure Temp
oC (ASTM)
Cure Time, Mins.
Hardness (Shore A)
Tensile Strenght (kg/cm2)
Elongation at Break (%)

1.0
1.0

150
20
60
168
580

0.7
0.5

150
20
60
176
610

Physical Testing After Ageing at 100oC for 70 hrs.

  • Hardness (Shore A)
  • Tensile Strength (kg/cm2)
  • Elongation at break (%)

63 (+3)
153 (-9%)
380 (-34%)

63 (+3)
160 (-9%)
390 (-35%)

Compression Set at 70oC for 48 hrs, 25% Deflection ASTMD - 395, (%)

22.70

16.80

*Observation Remarks: CCS provide better before ageing properties as compared to MS Sulphur. Inspite of lower anti-oxidants/anti-ozonants, properties are similar after ageing.


Formula:
Nitrile Rubber (Medium): 100, ZnO: 5, Strearic Acid: 1, HAF: 30, DOP: 10, CBS: 1.2, TMT: 1.2, Sulphur: 1.5

Properties

MC

SCCARE CCS

CLAY, phr

60

70

Physical Testing Before Ageing
Cure TempoC
Cure Time, Mins.
Hardness (Shore A)
Tensile Strenght (kg/cm2)
Elongation at Break (%)
Compression Set, 25% Deflection at 100oC for 24 hrs (%)

150
20
68
92
380
52.10

150
20
69
98
375
50.17

*Observation Remark: Additional China Clay does not deter CCS


SWASTIKA CONSTANT CARE

Contact Us

( *represents compulsory fields )

Tips on getting accurate quotes. Please include product name, order quantity, usage, special requests if any in your inquiry.



Contact Details
15, 4th Floor, Free School Street, Kolkata - 700016, West Bengal, India
Mr. Siddharth V. Jeloka (C.E.O.)
Mobile :+917210113577
Phone :+917210113577
Fax :91-33-65351418
Trust Stamp
Product Showcase
Send Inquiry    Call Me Free Offline Send SMS